Product features:

1.Waterborne, non-toxic, zero VOC emissions, fast drying time, excellent wetting and permeability to the steel substrate.
2.One-time film forming can be as high as 80um, no hanging, no cracking.
3.With good water resistance, film 100um, dry after 1h can be soaked for a long time, can not bubble, do not fall off, and hardness up to more than 4h.
4.The product performance in the same kind of coatings at home and abroad with superior cost performance.

Application scope:

1.Inorganic zinc rich coating
2.Inorganic zinc rich thick paste type primer
3.Inorganic high temperature resistant coating

Product specification:

Appearance: milky white liquid

Viscosity :(25℃, coated -4 cups), s  13-15

PH: 10-12

Solid content,% : ≥32

Modulus,M: 5.2

Specific gravity 1.1-1.2

Dilute solvent: a small amount of water

Recommend formula: E777-4waterborne inorganic zinc-rich coating resin is a semi-finished product. When used, only 30% : 70% or 26% : 74% zinc powder of the semi-finished product can be used (500-1250-mesh zinc powder is recommended) without adding any resin or auxiliary agent.

Validity: 6 months in a cool and ventilated environment

Packing specification: 200kg plastic drum

Legal declaration: this information is based on our knowledge and provide, the specific production formula and production process by each manufacturer according to their own needs before the production of the test, we can not be used as legal guarantee.